Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes

Hongyan Li; Xinni Tang; Yuanqing Chen

doi:doi:10.11648/j.ijmsa.20170602.15

| Peer-Reviewed

Chemical Solution Deposition of Epitaxial YBa₂Cu₃O_7-x /CeO₂/ La₂Zr₂O₇ Multilayer Films on Biaxially-Textured Ni-W Tapes

Hongyan Li, Xinni Tang, Yuanqing Chen

Published in International Journal of Materials Science and Applications (Volume 6, Issue 2)

Received: 4 February 2017 Accepted: 17 February 2017 Published: 2 March 2017

Views: Downloads:

Download PDF

Share This Article

Twitter
Linked In
Facebook

Abstract

CeO₂/La₂Zr₂O₇ composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa₂Cu₃O_7-x (YBCO) films were then deposited on the CeO₂/La₂Zr₂O₇ composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO₂ layers was investigated. It was found that CeO₂ film annealed at 1000°C under the atmosphere of N₂ containing of 5vol. %H₂ shows a high degree of c-orientation on La₂Zr₂O₇ (LZO) film. Effect of oxygen partial pressure on the properties of YBCO films deposited on the CeO₂/LZO buffer layers was also investigated. The YBCO annealed under N₂ containing of 500ppm O₂ shows the optimal properties, with critical current density (J_c) of 1MA/cm² at 77K, 0T.

Published in	International Journal of Materials Science and Applications (Volume 6, Issue 2)
DOI	10.11648/j.ijmsa.20170602.15
Page(s)	95-98
Creative Commons	This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.
Copyright	Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Superconductor, Film, Texture, Critical Current Density

References

[1]	V. Narayanan, IV. Driessche Prog Solid State Chem. 40 (2012) 57.
[2]	M. P. Paranthaman, T. Izumi, MRS Bulletin 29 (2004) 533.
[3]	T. Muroga, T. Araki, T. Niwa, Y. Iijima, T. Saito, I. Hirabayashi, Y. Yamada, Y. Shiohara, IEEE Transactions on Applied Superconductivity 13 (2003) 2532.
[4]	W. Prusseit, G. Sigl, R. Nemetschek, C. Hoffmann, J. Handke, A. Lumkemann, H. Kinder, IEEE Transactions on Applied Superconductivity 15 (2005) 2608.
[5]	S. Morlens, L. Ortega, B. Rousseau, S. Phok, J. L. Deschanvre, P. Chaudouet, P. Odier, Materials Science and Engineering B 104 (2003) 185.
[6]	S. M. Lim, H. S. Kim, K. C. Chung, B. S. Lee, D. Youm, Superconductor Science and Technology 17 (2004) 148.
[7]	C. Cai, R. I. Chakalova, G. Kong, K. Kawano, T. W. Button, J. S. Abell, E. Maher, Physica C 372–376 (2002) 786.
[8]	YQ Chen, XN. Tang, WB. Bian, MJ. Li, P. Jiang, GY Zhao, Supercond. Sci. Technol. 28 (2015) 075015.
[9]	YQ. Chen, CB. Wu, GY. Zhao, CY. You, Supercond. Sci. Technol 25 (2012) 062001.
[10]	K. Knoth, R. Huhnea, S. Oswald, L. Schultz, B. Holzapfel, Acta Materialia 55 (2007) 517–529.
[11]	Y. Chen, X. Yin, Y. Feng, W. Bian, M. Li, J. Niu, J Sol-Gel Sci. Technol.74 (2015) 249–255.

Cite This Article

Plain Text BibTeX RIS

APA Style

Hongyan Li, Xinni Tang, Yuanqing Chen. (2017). Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes. International Journal of Materials Science and Applications, 6(2), 95-98. https://doi.org/10.11648/j.ijmsa.20170602.15

Copy | Download

ACS Style

Hongyan Li; Xinni Tang; Yuanqing Chen. Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes. Int. J. Mater. Sci. Appl. 2017, 6(2), 95-98. doi: 10.11648/j.ijmsa.20170602.15

Copy | Download

AMA Style

Hongyan Li, Xinni Tang, Yuanqing Chen. Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes. Int J Mater Sci Appl. 2017;6(2):95-98. doi: 10.11648/j.ijmsa.20170602.15

Copy | Download

@article{10.11648/j.ijmsa.20170602.15,
  author = {Hongyan Li and Xinni Tang and Yuanqing Chen},
  title = {Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes},
  journal = {International Journal of Materials Science and Applications},
  volume = {6},
  number = {2},
  pages = {95-98},
  doi = {10.11648/j.ijmsa.20170602.15},
  url = {https://doi.org/10.11648/j.ijmsa.20170602.15},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20170602.15},
  abstract = {CeO2/La2Zr2O7 composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa2Cu3O7-x (YBCO) films were then deposited on the CeO2/La2Zr2O7 composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO2 layers was investigated. It was found that CeO2 film annealed at 1000°C under the atmosphere of N2 containing of 5vol. %H2 shows a high degree of c-orientation on La2Zr2O7 (LZO) film. Effect of oxygen partial pressure on the properties of YBCO films deposited on the CeO2/LZO buffer layers was also investigated. The YBCO annealed under N2 containing of 500ppm O2 shows the optimal properties, with critical current density (Jc) of 1MA/cm2 at 77K, 0T.},
 year = {2017}
}

Copy | Download

TY  - JOUR
T1  - Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes
AU  - Hongyan Li
AU  - Xinni Tang
AU  - Yuanqing Chen
Y1  - 2017/03/02
PY  - 2017
N1  - https://doi.org/10.11648/j.ijmsa.20170602.15
DO  - 10.11648/j.ijmsa.20170602.15
T2  - International Journal of Materials Science and Applications
JF  - International Journal of Materials Science and Applications
JO  - International Journal of Materials Science and Applications
SP  - 95
EP  - 98
PB  - Science Publishing Group
SN  - 2327-2643
UR  - https://doi.org/10.11648/j.ijmsa.20170602.15
AB  - CeO2/La2Zr2O7 composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa2Cu3O7-x (YBCO) films were then deposited on the CeO2/La2Zr2O7 composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO2 layers was investigated. It was found that CeO2 film annealed at 1000°C under the atmosphere of N2 containing of 5vol. %H2 shows a high degree of c-orientation on La2Zr2O7 (LZO) film. Effect of oxygen partial pressure on the properties of YBCO films deposited on the CeO2/LZO buffer layers was also investigated. The YBCO annealed under N2 containing of 500ppm O2 shows the optimal properties, with critical current density (Jc) of 1MA/cm2 at 77K, 0T.
VL  - 6
IS  - 2
ER  -

Copy | Download

Author Information

Hongyan Li

School of Materials Science and Technology, Xi’an University of Technology, Xi’an, China
Xinni Tang

School of Materials Science and Technology, Xi’an University of Technology, Xi’an, China
Yuanqing Chen

School of Materials Science and Technology, Xi’an University of Technology, Xi’an, China

Download PDF

Sections

Plain Text BibTeX RIS

APA Style

Hongyan Li, Xinni Tang, Yuanqing Chen. (2017). Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes. International Journal of Materials Science and Applications, 6(2), 95-98. https://doi.org/10.11648/j.ijmsa.20170602.15

Copy | Download

ACS Style

Hongyan Li; Xinni Tang; Yuanqing Chen. Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes. Int. J. Mater. Sci. Appl. 2017, 6(2), 95-98. doi: 10.11648/j.ijmsa.20170602.15

Copy | Download

AMA Style

Hongyan Li, Xinni Tang, Yuanqing Chen. Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes. Int J Mater Sci Appl. 2017;6(2):95-98. doi: 10.11648/j.ijmsa.20170602.15

Copy | Download

@article{10.11648/j.ijmsa.20170602.15,
  author = {Hongyan Li and Xinni Tang and Yuanqing Chen},
  title = {Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes},
  journal = {International Journal of Materials Science and Applications},
  volume = {6},
  number = {2},
  pages = {95-98},
  doi = {10.11648/j.ijmsa.20170602.15},
  url = {https://doi.org/10.11648/j.ijmsa.20170602.15},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20170602.15},
  abstract = {CeO2/La2Zr2O7 composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa2Cu3O7-x (YBCO) films were then deposited on the CeO2/La2Zr2O7 composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO2 layers was investigated. It was found that CeO2 film annealed at 1000°C under the atmosphere of N2 containing of 5vol. %H2 shows a high degree of c-orientation on La2Zr2O7 (LZO) film. Effect of oxygen partial pressure on the properties of YBCO films deposited on the CeO2/LZO buffer layers was also investigated. The YBCO annealed under N2 containing of 500ppm O2 shows the optimal properties, with critical current density (Jc) of 1MA/cm2 at 77K, 0T.},
 year = {2017}
}

Copy | Download

TY  - JOUR
T1  - Chemical Solution Deposition of Epitaxial YBa2Cu3O7-x /CeO2/ La2Zr2O7 Multilayer Films on Biaxially-Textured Ni-W Tapes
AU  - Hongyan Li
AU  - Xinni Tang
AU  - Yuanqing Chen
Y1  - 2017/03/02
PY  - 2017
N1  - https://doi.org/10.11648/j.ijmsa.20170602.15
DO  - 10.11648/j.ijmsa.20170602.15
T2  - International Journal of Materials Science and Applications
JF  - International Journal of Materials Science and Applications
JO  - International Journal of Materials Science and Applications
SP  - 95
EP  - 98
PB  - Science Publishing Group
SN  - 2327-2643
UR  - https://doi.org/10.11648/j.ijmsa.20170602.15
AB  - CeO2/La2Zr2O7 composite buffer layers were deposited on Ni-W tapes using chemical solution method. YBa2Cu3O7-x (YBCO) films were then deposited on the CeO2/La2Zr2O7 composite buffer layers using a low-fluorine solution route. Effect of the annealing temperature and annealing atmosphere on the texture of the CeO2 layers was investigated. It was found that CeO2 film annealed at 1000°C under the atmosphere of N2 containing of 5vol. %H2 shows a high degree of c-orientation on La2Zr2O7 (LZO) film. Effect of oxygen partial pressure on the properties of YBCO films deposited on the CeO2/LZO buffer layers was also investigated. The YBCO annealed under N2 containing of 500ppm O2 shows the optimal properties, with critical current density (Jc) of 1MA/cm2 at 77K, 0T.
VL  - 6
IS  - 2
ER  -

Copy | Download