Effect of Die Bearing Parameters on Corrosion Response of Extruded Al-Zn-Mg Alloy
International Journal of Materials Science and Applications
Volume 4, Issue 3, May 2015, Pages: 209-212
Received: May 5, 2015;
Accepted: May 11, 2015;
Published: May 27, 2015
Views 4501 Downloads 126
Injor Oryina Mbaadega, Department of Metallurgical and Materials Engineering, Federal University of Technology, Akure, Nigeria
Adewuyi Benjamin Omotayo, Department of Metallurgical and Materials Engineering, Federal University of Technology, Akure, Nigeria
Gundu David Terfa, Department of Mechanical Engineering, University of Agriculture, Makurdi, Nigeria
In this paper, the effect of die bearing parameters (die bearing length and die reduction ratio) on corrosion response of extruded Al-Zn-Mg alloy was investigated. The alloy was target material for production of automobile bumper beams. Medium carbon steel dies with entry angles of 750, 900, 1050, 1200, 1500 and reduction ratios of 0.21, 0.40, 0.48 and 0.62 were used to extrude the alloy at temperature of 5000C. The extruded samples were subjected to electrochemical corrosion using Tafel polarization technique. The potential dynamic polarization curves indicated improvement in the corrosion resistance of the extruded alloy, and the corrosion rate under extruded condition increased with increase in both die angle and reduction ratio. It was concluded that the Al-Zn-Mg alloy is suitable for the target application.
Injor Oryina Mbaadega,
Adewuyi Benjamin Omotayo,
Gundu David Terfa,
Effect of Die Bearing Parameters on Corrosion Response of Extruded Al-Zn-Mg Alloy, International Journal of Materials Science and Applications.
Vol. 4, No. 3,
2015, pp. 209-212.
Stansbury E.E and Buchanan R.A. (2000). Fundamentals of Electrochemical Corrosion ASM. International Materials Park, USA.
Conde, A., Fernandez, B. and De Damborenea, J. (1998): Corrosion Science, 40: 91.
Naeem, H. T., Mohammed, K. S., Ahmad, K. R. and Rahmat, A. (2014): Corrosion Behaviour of The Al-Zn-Mg-Cu Alloys With Nickel Additions. Digest Journal of Nanomaterials and Biostructures. 9(4): 1309 - 1315.
AFSA Corrosion Pocket Guide (2011): Corrosion Resistance of Aluminium and Protective Measures where Appropriate. 1st Edition, Aluminium Federation of South Africa, 36p.
Nadia, H. H. (2011): Corrosion inhibition and adsorption behavior of methionine on Mg- Al-Zn alloy. Journal of Chemical Engineering and Materials Science Vol. 2(2): 28-38.
Badawy, W. A., Nady, H. and Abd El-Hafez, G. M. (2014): Corrosion Inhibition of Mg-Al-Zn Alloy in Neutral Chloride Solutions by N-Acetyl-Cysteine as Eco-Friendly Material. International Journal of Engineering and Innovative Technology (IJEIT), 4(3): 125-132.
Sameljuk, A.V., Neikov, O.D., Krajnikov, A.V., Milman, Yu.V. and Thompson, G.E. (2004): Corrosion behaviour of powder metallurgical and cast Al–Zn–Mg base alloys. Corrosion Science. 46: 147–158.
Rudd, A.L., Breslin, C.B. and Mansfeld, F. (2000): The corrosion protection afforded by rare earth conversion coatings applied to magnesium Corrosion Science, 42: 257.
Yfantis, A., Paloumpa, I., Schmei, D, and Yfantis, D. (2002). Novel corrosion resistant films for Mg alloys. Surface and Coatings Technology, 151-152: 400-404.
Gundu, T., Tuleun, L. and Injor, O. (2014): Effect of Pocket Die Bearing Geometry on Direct Cold Extrusion Process Responses. American Journal of Mechanical Engineering. 2-3-3: 65-69.
Flitta, I. and Sheppard, T. (2003): Nature of friction in extrusion process and its effect on material flow. Materials Science and Technology 19: 837-846.
Piwnik, J. and Mogielnicki, K. (2010): The friction influence of stress in micro extrusion. Archives of Foundry Engineering 10(1): 451-454.
El- Sayed (1997): Phenothiazine as inhibitor of the corrosion of cadmium in acidic solutions. J. Appl. Electrochem., 27: 193-200.
Alvarez, J. O., Gonzalez, C., Aramburu, G., Herrera, R., Juarez‐Islas, J.A. (2005): The effect of adding different Mg contents to an Al‐12wt.% Zn master alloy. Materials Science and Engineering A402: 320‐324.
Pardo A., Merino M.C., Merino S., Lopez M.D., Viejo F. and Carboneras M. (2003): Influence of reinforcement grade and matrix composition on corrosion resistance of cast aluminium matrix composites (A3xx.x/SiCp) in a humid environment. Mater. Corros., 54: 311-317.