The work was done to understand the effects of naturally occurred bone and teeth ash on the physical as well as mechanical properties of bone china products. Both bone and teeth ash was prepared following conventional thermal decomposition method. Locally found cattle bones and tooth was utilized for this purpose. Three different routes of powder or ash preparation i.e. boiling-wood firing, excavating-calcination and boiling-calcination were followed. The calcination temperature was fixed at 950°C-2 hours. After that, density and phase identification of ash was carried out. Finally, bone china product was manufactured using powder compaction and slip casting route. Firing was done at a constant temperature (1150°C-2 hours). Further characterizations (density, percent firing shrinkage, percent water absorption and modulus of rupture measurement) of the sintered samples were evaluated. Boiling-calcination route was found to be the most superlative route. However, enhanced properties of bone china were obtained by the addition of teeth ash.
| Published in | International Journal of Materials Science and Applications (Volume 6, Issue 4) |
| DOI | 10.11648/j.ijmsa.20170604.12 |
| Page(s) | 171-177 |
| Creative Commons |
This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited. |
| Copyright |
Copyright © The Author(s), 2024. Published by Science Publishing Group |
Nitrogen (N2) Pycnomerty, X-ray Diffraction (XRD), Firing Shrinkage, Water Absorption, Modulus of Rupture (MOR)
| [1] | T. Ifka, M. T. Palou and Z. Bazelova, “The influence of CaO and P2O5 of bone ash upon the reactivity and burnability of cement raw mixtures,” Ceramics-Silikaty, vol. 56 (1), pp. 76-84, 2012. |
| [2] | J. F. Shackelford, Advanced Ceramics-BIOCERAMICS, Gordon and Breach Science Publishers, USA, vol. 1, pp. 19-20, 2005. |
| [3] | A. Sobczak, Z. Kowalski and Z. Wzorek, “Preparation of hydroxyapatite from animal bones,” Acta of Bioengineering and Biomechanics, vol. 11(4), 2009. |
| [4] | C. B. Carter and M. G. Norton, Ceramic Materials Science and Engineering, Springer, pp. 635-649, 2007. |
| [5] | I. O. Oladele, “Development of Bone Ash and Bone Particulate Reinforced Polyester Composites for Biomedical Applications,” Leonardo Electronic Journal of Practices and Technologies, pp. 15-26, 2013. |
| [6] | G. M. Ayininuola and A. O. Denloye, “Influence of Bone Ash on Soil California Bearing Ratio,” JETEAS, vol. 5 (8), 2014, pp. 235-237. |
| [7] | E. Blakelock, “Analysis of Bone-ash Cupels and Porcelain Associated with the Isleworth Pottery Works, Middlesex”, Centre for Archaeology Report, vol. 20, 2005. |
| [8] | D. Gouvêa, S. Bernard, G. A. V. Alatrista and S. M. Toffoli, “Effect of Calcination Temperature on the Properties of Bovine Bone Ash for the Fabrication of Bone China,” Ceramica, vol. 54, pp. 86-91, 2008. |
| [9] | Z. Zakariaa, H. Haronb, “Characterisation of Local Bone Ash for Bone China Production,” Jurnal teknologi (Sciences & Engineering), vol. 66 (1), pp. 25-34, 2014. |
| [10] | C. Lorprayoon, “Phases of Cattle Bones at Elevated Temperatures,” J. Sci. Soc., vol.12, pp.159-170, 1986. |
| [11] | E. Hayek, and H. Newesely, “Pentacalcium Hydroxyorthophosphate,” Inorganic synthesis, vol. 7, Mc Graw-Hill book company Inc., New York, pp. 63, 1963. |
| [12] | Lehr et al., “Crystallographic Properties of Fertilizer Compounds,” Thenn. Vall. Auth. Chem. Engr. Bull. Vol. 6, pp.166, 1967. |
| [13] | Mosebach, “Some Properties of the Crystals of Synthetic Hydroxyapatite,” Bull. Group. Int. Rech. Sci. Stomatol., vol. 9, pp. 415-19. |
| [14] | R. I. M. Asri, W. S. W. Harun, M. A. Hassan, S. A. C. Ghani and Z. Buyong, “A review of hydroxyapatite-based coating techniques: Sol–gel and electrochemical depositions on biocompatible metals,” Journal of the Mechanical Behavior of Biomedical Materials, vol. 57, pp. 95-108, 2016. |
| [15] | S. Ahmadi, I. Mohammadi and S. K. Sadmezhaad, “Hydroxyapatite based and anodic Titania nanotube biocomposite coatings: Fabrication, characterization and electrochemical behavior,” Surface and Coatings Technology, vol. 287, pp. 67-75, 2016. |
| [16] | Z. C. Xiong, Y. J. Zhu, F. F. Chen, T. W. Sun and Y. Q. Shen, “One-step synthesis of silver nanoparticle-decorated hydroxyapatite nanowires for the construction of highly flexible free-standing paper with high antibacterial activity,” Chem. Eur. J., vol. 22, pp. 11224 -11231, 2016. |
APA Style
Mst. Sharmin Mostari, Tasmia Zaman, Md. Shamimur Rahman. (2017). Synthesis and Characterization of Bone & Teeth Ash and Analysis of Their Influence on the Properties of Bone China. International Journal of Materials Science and Applications, 6(4), 171-177. https://doi.org/10.11648/j.ijmsa.20170604.12
ACS Style
Mst. Sharmin Mostari; Tasmia Zaman; Md. Shamimur Rahman. Synthesis and Characterization of Bone & Teeth Ash and Analysis of Their Influence on the Properties of Bone China. Int. J. Mater. Sci. Appl. 2017, 6(4), 171-177. doi: 10.11648/j.ijmsa.20170604.12
AMA Style
Mst. Sharmin Mostari, Tasmia Zaman, Md. Shamimur Rahman. Synthesis and Characterization of Bone & Teeth Ash and Analysis of Their Influence on the Properties of Bone China. Int J Mater Sci Appl. 2017;6(4):171-177. doi: 10.11648/j.ijmsa.20170604.12
Share This Article
Twitter
Linked In
Facebook
Copy
Download@article{10.11648/j.ijmsa.20170604.12,
author = {Mst. Sharmin Mostari and Tasmia Zaman and Md. Shamimur Rahman},
title = {Synthesis and Characterization of Bone & Teeth Ash and Analysis of Their Influence on the Properties of Bone China},
journal = {International Journal of Materials Science and Applications},
volume = {6},
number = {4},
pages = {171-177},
doi = {10.11648/j.ijmsa.20170604.12},
url = {https://doi.org/10.11648/j.ijmsa.20170604.12},
eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijmsa.20170604.12},
abstract = {The work was done to understand the effects of naturally occurred bone and teeth ash on the physical as well as mechanical properties of bone china products. Both bone and teeth ash was prepared following conventional thermal decomposition method. Locally found cattle bones and tooth was utilized for this purpose. Three different routes of powder or ash preparation i.e. boiling-wood firing, excavating-calcination and boiling-calcination were followed. The calcination temperature was fixed at 950°C-2 hours. After that, density and phase identification of ash was carried out. Finally, bone china product was manufactured using powder compaction and slip casting route. Firing was done at a constant temperature (1150°C-2 hours). Further characterizations (density, percent firing shrinkage, percent water absorption and modulus of rupture measurement) of the sintered samples were evaluated. Boiling-calcination route was found to be the most superlative route. However, enhanced properties of bone china were obtained by the addition of teeth ash.},
year = {2017}
}
TY - JOUR T1 - Synthesis and Characterization of Bone & Teeth Ash and Analysis of Their Influence on the Properties of Bone China AU - Mst. Sharmin Mostari AU - Tasmia Zaman AU - Md. Shamimur Rahman Y1 - 2017/06/29 PY - 2017 N1 - https://doi.org/10.11648/j.ijmsa.20170604.12 DO - 10.11648/j.ijmsa.20170604.12 T2 - International Journal of Materials Science and Applications JF - International Journal of Materials Science and Applications JO - International Journal of Materials Science and Applications SP - 171 EP - 177 PB - Science Publishing Group SN - 2327-2643 UR - https://doi.org/10.11648/j.ijmsa.20170604.12 AB - The work was done to understand the effects of naturally occurred bone and teeth ash on the physical as well as mechanical properties of bone china products. Both bone and teeth ash was prepared following conventional thermal decomposition method. Locally found cattle bones and tooth was utilized for this purpose. Three different routes of powder or ash preparation i.e. boiling-wood firing, excavating-calcination and boiling-calcination were followed. The calcination temperature was fixed at 950°C-2 hours. After that, density and phase identification of ash was carried out. Finally, bone china product was manufactured using powder compaction and slip casting route. Firing was done at a constant temperature (1150°C-2 hours). Further characterizations (density, percent firing shrinkage, percent water absorption and modulus of rupture measurement) of the sintered samples were evaluated. Boiling-calcination route was found to be the most superlative route. However, enhanced properties of bone china were obtained by the addition of teeth ash. VL - 6 IS - 4 ER -
Information
Email: