Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete

Yang Jinglin; Tang Feng; Wan Linhui; Fang Liang; Ou Yangguoyuan

doi:doi:10.11648/j.sd.20170507.31

| Peer-Reviewed |

Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete

Yang Jinglin, Tang Feng, Wan Linhui, Fang Liang, Ou Yangguoyuan

Received: 28 December 2017 Accepted: Published: 29 December 2017

Views: Downloads:

Download PDF

Share This Article

Twitter
Linked In
Facebook

Abstract

Pedestrian road paving brick is a kind of paving material. It is made of cement, stone and sand as raw material, and it is cut into stripes or squares by vibrating forming surface. According to the construction waste recycled aggregate concrete, the water cement ratio, recycled aggregate replacement rate as the main parameters, design a new type of plate nail experimental study on pedestrian road brick, road brick design has 4 panels and 6 plate nail nails, nail plate thickness were designed as 1mm, 1.5mm and 2mm. The influence of different water binder ratio and recycled aggregate replacement rate on the compressive strength and skid strength of the new pavement brick was analyzed by orthogonal test. The experimental results show that the compressive strength and slip strength of the new type of pavement brick decrease with the replacement rate of recycled aggregate concrete gradually increasing. Nail type plate relative to the compressive strength of brick without road brick plate nail is similar, but the anti slip strength increased; the nail plate thickness on pavement brick tile anti sliding strength were improved, the total efficiency coefficient is similar.

DOI	10.11648/j.sd.20170507.31
Published in	Science Discovery (Volume 5, Issue 7, December 2017)
Page(s)	598-602
Creative Commons	This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.
Copyright	Copyright © The Author(s), 2024. Published by Science Publishing Group

Keywords

Construction Waste, Recycled Aggregate, Concrete, New Road Brick, Experiment, Strength

References

[1]	李海明.我国城市建筑垃圾资源化利用研究进展与展望[J].建筑技术，2013,44(9):795-797。
[2]	郭昊，李英子.北京市建筑垃圾资源化研究[J].经济师，2014,(1):21-22。
[3]	赵海英，薛俭.我国在建筑垃圾资源化中存在的问题及对策研究[J].施工技术，2010,(S2):472-473。
[4]	蒲云辉，唐嘉陵.日本建筑垃圾资源化对我国的启示[J].建筑技术，2012,41(376):43-45。
[5]	张亚梅，秦鸿根，孙伟等.再生混凝土配合比设计初探[J].混凝土与水泥制品，2002,123(1):7-9。
[6]	朱平华，谢飞飞.再生混凝土路面砖性能研究[J].混凝土，2015,(12):134-137。
[7]	何霞，朱从香，王兵.再生混凝土路面砖抗碳化性能试验研究[J].建筑技术，2017,48(5):523-527。
[8]	崔正龙，路沙沙，汪振双.再生骨料特性对再生混凝土强度和碳化性能的影响[J].建筑材料学报，2012,(4):264-267。
[9]	王江，薛燕飞，周辉.再生混凝土抗压强度研究[J].混凝土，2006,(7):47-48。
[10]	周静海，王晓天，郭易奇，康天蓓.再生混凝土抗压强度的影响因素的有限元分析[J].混凝土，2017,(6):1-4。
[11]	董振平，赵凯月，王艳，康天蓓.再生塑料混凝土研究现状[J].混凝土，2017,(3):100-104。
[12]	李佳彬，肖建庄，黄键.再生粗骨料取代率对混凝土抗压强度的影响[J].建筑材料学报，2006,(3):297-301。

Cite This Article

Plain Text BibTeX RIS

APA Style

Yang Jinglin, Tang Feng, Wan Linhui, Fang Liang, Ou Yangguoyuan. (2017). Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete. Science Discovery, 5(7), 598-602. https://doi.org/10.11648/j.sd.20170507.31

Copy | Download

ACS Style

Yang Jinglin; Tang Feng; Wan Linhui; Fang Liang; Ou Yangguoyuan. Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete. Sci. Discov. 2017, 5(7), 598-602. doi: 10.11648/j.sd.20170507.31

Copy | Download

AMA Style

Yang Jinglin, Tang Feng, Wan Linhui, Fang Liang, Ou Yangguoyuan. Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete. Sci Discov. 2017;5(7):598-602. doi: 10.11648/j.sd.20170507.31

Copy | Download

@article{10.11648/j.sd.20170507.31,
  author = {Yang Jinglin and Tang Feng and Wan Linhui and Fang Liang and Ou Yangguoyuan},
  title = {Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete},
  journal = {Science Discovery},
  volume = {5},
  number = {7},
  pages = {598-602},
  doi = {10.11648/j.sd.20170507.31},
  url = {https://doi.org/10.11648/j.sd.20170507.31},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.sd.20170507.31},
  abstract = {Pedestrian road paving brick is a kind of paving material. It is made of cement, stone and sand as raw material, and it is cut into stripes or squares by vibrating forming surface. According to the construction waste recycled aggregate concrete, the water cement ratio, recycled aggregate replacement rate as the main parameters, design a new type of plate nail experimental study on pedestrian road brick, road brick design has 4 panels and 6 plate nail nails, nail plate thickness were designed as 1mm, 1.5mm and 2mm. The influence of different water binder ratio and recycled aggregate replacement rate on the compressive strength and skid strength of the new pavement brick was analyzed by orthogonal test. The experimental results show that the compressive strength and slip strength of the new type of pavement brick decrease with the replacement rate of recycled aggregate concrete gradually increasing. Nail type plate relative to the compressive strength of brick without road brick plate nail is similar, but the anti slip strength increased; the nail plate thickness on pavement brick tile anti sliding strength were improved, the total efficiency coefficient is similar.},
 year = {2017}
}

Copy | Download

TY  - JOUR
T1  - Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete
AU  - Yang Jinglin
AU  - Tang Feng
AU  - Wan Linhui
AU  - Fang Liang
AU  - Ou Yangguoyuan
Y1  - 2017/12/29
PY  - 2017
N1  - https://doi.org/10.11648/j.sd.20170507.31
DO  - 10.11648/j.sd.20170507.31
T2  - Science Discovery
JF  - Science Discovery
JO  - Science Discovery
SP  - 598
EP  - 602
PB  - Science Publishing Group
SN  - 2331-0650
UR  - https://doi.org/10.11648/j.sd.20170507.31
AB  - Pedestrian road paving brick is a kind of paving material. It is made of cement, stone and sand as raw material, and it is cut into stripes or squares by vibrating forming surface. According to the construction waste recycled aggregate concrete, the water cement ratio, recycled aggregate replacement rate as the main parameters, design a new type of plate nail experimental study on pedestrian road brick, road brick design has 4 panels and 6 plate nail nails, nail plate thickness were designed as 1mm, 1.5mm and 2mm. The influence of different water binder ratio and recycled aggregate replacement rate on the compressive strength and skid strength of the new pavement brick was analyzed by orthogonal test. The experimental results show that the compressive strength and slip strength of the new type of pavement brick decrease with the replacement rate of recycled aggregate concrete gradually increasing. Nail type plate relative to the compressive strength of brick without road brick plate nail is similar, but the anti slip strength increased; the nail plate thickness on pavement brick tile anti sliding strength were improved, the total efficiency coefficient is similar.
VL  - 5
IS  - 7
ER  -

Copy | Download

Author Information

Yang Jinglin

College of Engineering, Hunan Agriculture University, Changsha, China
Tang Feng

College of Engineering, Hunan Agriculture University, Changsha, China
Wan Linhui

College of Engineering, Hunan Agriculture University, Changsha, China
Fang Liang

College of Engineering, Hunan Agriculture University, Changsha, China
Ou Yangguoyuan

College of Engineering, Hunan Agriculture University, Changsha, China

Download PDF

Sections

Plain Text BibTeX RIS

APA Style

Yang Jinglin, Tang Feng, Wan Linhui, Fang Liang, Ou Yangguoyuan. (2017). Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete. Science Discovery, 5(7), 598-602. https://doi.org/10.11648/j.sd.20170507.31

Copy | Download

ACS Style

Yang Jinglin; Tang Feng; Wan Linhui; Fang Liang; Ou Yangguoyuan. Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete. Sci. Discov. 2017, 5(7), 598-602. doi: 10.11648/j.sd.20170507.31

Copy | Download

AMA Style

Yang Jinglin, Tang Feng, Wan Linhui, Fang Liang, Ou Yangguoyuan. Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete. Sci Discov. 2017;5(7):598-602. doi: 10.11648/j.sd.20170507.31

Copy | Download

@article{10.11648/j.sd.20170507.31,
  author = {Yang Jinglin and Tang Feng and Wan Linhui and Fang Liang and Ou Yangguoyuan},
  title = {Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete},
  journal = {Science Discovery},
  volume = {5},
  number = {7},
  pages = {598-602},
  doi = {10.11648/j.sd.20170507.31},
  url = {https://doi.org/10.11648/j.sd.20170507.31},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.sd.20170507.31},
  abstract = {Pedestrian road paving brick is a kind of paving material. It is made of cement, stone and sand as raw material, and it is cut into stripes or squares by vibrating forming surface. According to the construction waste recycled aggregate concrete, the water cement ratio, recycled aggregate replacement rate as the main parameters, design a new type of plate nail experimental study on pedestrian road brick, road brick design has 4 panels and 6 plate nail nails, nail plate thickness were designed as 1mm, 1.5mm and 2mm. The influence of different water binder ratio and recycled aggregate replacement rate on the compressive strength and skid strength of the new pavement brick was analyzed by orthogonal test. The experimental results show that the compressive strength and slip strength of the new type of pavement brick decrease with the replacement rate of recycled aggregate concrete gradually increasing. Nail type plate relative to the compressive strength of brick without road brick plate nail is similar, but the anti slip strength increased; the nail plate thickness on pavement brick tile anti sliding strength were improved, the total efficiency coefficient is similar.},
 year = {2017}
}

Copy | Download

TY  - JOUR
T1  - Experimental Study on Construction Waste Making New Road Brick with Recycled Aggregate Concrete
AU  - Yang Jinglin
AU  - Tang Feng
AU  - Wan Linhui
AU  - Fang Liang
AU  - Ou Yangguoyuan
Y1  - 2017/12/29
PY  - 2017
N1  - https://doi.org/10.11648/j.sd.20170507.31
DO  - 10.11648/j.sd.20170507.31
T2  - Science Discovery
JF  - Science Discovery
JO  - Science Discovery
SP  - 598
EP  - 602
PB  - Science Publishing Group
SN  - 2331-0650
UR  - https://doi.org/10.11648/j.sd.20170507.31
AB  - Pedestrian road paving brick is a kind of paving material. It is made of cement, stone and sand as raw material, and it is cut into stripes or squares by vibrating forming surface. According to the construction waste recycled aggregate concrete, the water cement ratio, recycled aggregate replacement rate as the main parameters, design a new type of plate nail experimental study on pedestrian road brick, road brick design has 4 panels and 6 plate nail nails, nail plate thickness were designed as 1mm, 1.5mm and 2mm. The influence of different water binder ratio and recycled aggregate replacement rate on the compressive strength and skid strength of the new pavement brick was analyzed by orthogonal test. The experimental results show that the compressive strength and slip strength of the new type of pavement brick decrease with the replacement rate of recycled aggregate concrete gradually increasing. Nail type plate relative to the compressive strength of brick without road brick plate nail is similar, but the anti slip strength increased; the nail plate thickness on pavement brick tile anti sliding strength were improved, the total efficiency coefficient is similar.
VL  - 5
IS  - 7
ER  -

Copy | Download