Volume 5, Issue 3, September 2020, Pages: 33-37
Received: Jan. 17, 2020;
Accepted: Jun. 8, 2020;
Published: Jul. 23, 2020
Views 163 Downloads 77
Ming Chen, Dongfeng Commercial Vehicle Technology Center, Wuhan, China
Wei Dong, Faculty of General Education, Wuhan International Trade University, Wuhan, China
Cherry Qin, SGS-CSTC Standards Technical Services Co., Ltd. Wuhan Branch, Wuhan, China
According to the following plating processes: deoiling → washing → pickling → washing → drying → weighing → electroless plating → washing → drying → weighing. It can obtain Ni-P deposit on aluminum alloy. It studied the influence of bath composition and process parameters on the composition and deposition rate of the alloy coating. Under temperature of 85~90°C, nickel sulfate hexahydrate 15~35g/L, sodium hypophosphite 10~30g/L, sodium citrate 5~10g/L, tartaric acid 1~2g/L, pH 3~5, reaction time 30~60min, load factor 1.0~2.0dm2/L. The microstructure, surface morphology, composition and valence of the elements in the alloy coating were studied by metallographic microscope, SEM, EDS and other modern analytical methods. The size of spherical grain was below 1um and compact distribution. The chemical coatings were mainly composed two elements, which were phosphorous and nickel. The mass percentage of phosphorous was about 15%, and the other one was about 80~85%. The corrosion resistance of the alloy coating was studied by CASS  test method, through 80h CASS test detection, the protection class of chemical coating can be reached 5. The relevant evaluation criteria can be referred to GB/T 6461-2002 . The results show that the Ni-P binary amorphous alloy can be successfully prepared by this process.
A Method for Electroless Nickel Plating on Aluminum Alloy Surface, Engineering Science.
Vol. 5, No. 3,
2020, pp. 33-37.
GB/T 12967.3-2008 Test methods for anodic oxidation coatings of aluminium and aluminium alloys-Part 3: Copper accelerated acetic acid salt spray test (CASS test).
GB/T 6461-2002 Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates-Rating of test specimens and manufactured articles subjected to corrosion tests.
L. C. Zhang, J. Xu. Glass-forming ability of melt-spun multicomponent (Ti, Zr, Hf)-(Cu, Ni, Co)-Al alloys with equiatomic substitution. Journal of Non-Crystalline Solids 347 (2004), 166-172.
L. C. Zhang, Z. Q. Shen, J. Xu. Mechanically milling-induced amorphization in Sn-containing Ti-based multicomponent alloy systems. Materials Science and Engineering A 394 (2005), 204-209.
A. Brenner, G. E. Riddell, J. Res. Natl. Bureau Standards 37 (1) (1946).
A. Brenner, G. E. Riddel. Nickel plating by chemical reduction. U. S. Patent 2532283a. Dec. 1950.
Jian-hui Lin, Chong Wang, Shouxu Wang. Initiation electroless nickel plating by atomic hydrogen PCB final finishing [J]. Chemical Engineering Journal, 2016, 306 (15): 117-123.
II-Cho Park, Seong-Jong Kim. Effect of lead nitrate concentration on electroless nickel plating characteristics of gray cast iron [J]. Surface and Coatings Technology, 2019, 376 (25): 2-7.
Shao-Feng Zhou, Qiao-Xin Zhang, Hao Liu. Microwave absorption performance of magnetic Fe-Ni-P nanoparticles electrolessly plated on hollow glass microspheres [J]. Materials Chemistry and Physics, 2012, 134 (1): 224-228.
Guo-Xun Zeng, Jian-Kun Yang, Ren-Peng Hong. Preparation and thermal reflectivity of nickel antimony titanium yellow rutile coate hollow glass microspheres composite pigment [J]. Ceramics International, 2018, 44 (8): 8788-8794.
So-Young Cheon, So-Yeon Park, Young-Mok Rhym. The effect of bath condition on the electroless nickel plating on the porous carbon substrate [J]. Current Applied Physics, 2011, 11 (3): 790-793.
Ce Gao, Lei Dai, Wei Meng. Electrochemically promote electroless nickel-phosphorous plating on titanium substrate [J]. Applied Surface Science, 2017, 392 (15): 912-919.
Lai-Ma Luo, Ze-Long Lu, Xiao-Yue Tan, Xiao-Yu Ding, Li-Mei Huang, Ji-Gui Cheng, Liu Zhu, Yu-Cheng Wu. A specific chemical activation pretreatment for electroless nickel plating on SiC ceramic powders [J]. Powder Technology, 2013, 249, 431-435.
Bo-Nian Hu, Rui-Xue Sun, Gang Yu, Ling-Song Liu. Effect of bath pH and stabilizer on electroless nickel plating of magnesium alloys [J]. Surface and Coatings Technology, 2013, 228, 84-91.
Zhong-Cai Shao, Zhi-Qiang Cai, Rong Hu, Shou-Qiang Wei. The study of electroless nickel plating directly on magnesium alloy [J]. Surface and Coatings Technology, 2014, 249, 42-47.
Ayushi Thakur, Swaroop Gharde, Balasubramanian Kandasubramanian. Electroless nickel fabrication on surface modified magnesium substrates [J]. Defence Technology, 2019, 15 (4): 636-644.
Ming-Qiu Wang, Jun Yan, Shi-Guo Du, Hao Qin. A novel process of electroless nickel plating on PVC with semi-IPN hydrogel pretreatment [J]. Journal of Alloys and Compounds, 2013, 557, 270-273.
Yong-Jun Zhang. High speed Ni-P electroless plating on 6063 aluminum alloy extruded profiles [J]. Materials Protection, 2018, 06, 54-58.
Peng-Ju Zhang. Study on electroless Ni-W-P alloy plating technology of 6061 aluminum alloy for automobile [J]. Electroplating and Environmental Protection, 2019, 04, 46-48.
Gang Liu. Study on electroless nickel plating on aluminum lithium alloy and corrosion resistance of film [J]. Electroplating and Finishing, 2018, 04, 12-17.