Abstract

Due to abundant raw materials, low cost and high theoretical energy density, organic potassium ion batteries (OPIBs) have attracted more and more attention from researchers as next promising battery system. However, some challenges still need to be solved. For example, most small-molecule organic electrode materials faced serious dissolution problem in liquid electrolytes, resulting in poor cycle stability. In particular, there are relatively few reports on the current cathodes with really excellent comprehensive performance (such as: high specific capacity, high working voltage, long life-span and excellent rate performance) for OPIBs. In this article, two polyanthraquinoneimide polymers were successfully synthesized and used as organic cathode materials for potassium ion batteries. Attributed to the large molecular structure of the polymer, PPAQ and PNAQ both were successful to be insoluble in the electrolyte (1 mol/L KPF6 in DME). After comparison, it was found that PNAQ exhibited better comprehensive electrochemical performance than PPAQ. At a current density of 100 mA/g, PNAQ achieved a stable discharge capacity of 138 mAh/g for 200 cycles and the retention rate was as high as 92%. At the same time, after 750 cycles at a high current density of 800 mA/g, the specific capacity of PNAQ still remained at 71 mAh/g with an average attenuation of only 0.03 mAh/g per cycle. Through an appropriate design process for the molecular structure, we proved that organic polymers could become excellent cathodes for potassium ion batteries.

Published in International Journal of Energy and Power Engineering (Volume 10, Issue 5)
DOI 10.11648/j.ijepe.20211005.11
Page(s) 79-86
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2021. Published by Science Publishing Group

Keywords

Polyquinoneimide, Organic Cathodes, Potassium-Ion Batteries

References
[1] D. Larcher, J. M. Tarascon. Towards greener and more sustainable batteries for electrical energy storage. Nat. Chem., 2015, 7: 19.
[2] M. Armand, J. M. Tarascon. Building better batteries. Nature, 2008, 451: 652.
[3] J. M. Tarascon, M. Armand. Issues and challenges facing rechargeable lithium batteries. Nature, 2001, 414: 359.
[4] L. Chen, L. L. Shaw. Recent advances in lithium-sulfur batteries. J. Power Sources, 2014, 267: 770.
[5] Y. S. Xu, S. Y. Duan, Y. G. Sun, D. S. Bin, X. S. Tao, D. Zhang, Y. Liu, A. M. Cao, L. J. Wan. Recent developments in electrode materials for potassium-ion batteries. J. Mater. Chem. A, 2019, 7: 4334.
[6] J. Y. Hwang, S. T. Myung, Y. Sun. Recent Progress in Rechargeable Potassium Batteries. Adv. Funct. Mater., 2018, 28: 1802938.
[7] X. Wu, Y. Chen, Z. Xing, C. W. K. Lam, S.-S. Pang, W. Zhang, Z. Ju. Advanced Carbon-Based Anodes for Potassium-Ion Batteries. Adv. Energy Mater., 2019, 9: 1900343.
[8] Y. Sun, S. Guo, H. Zhou. Exploration of Advanced Electrode Materials for Rechargeable Sodium-Ion Batteries. Adv. Energy Mater., 2019, 9: 1800212.
[9] Z. Jian, Z. Xing, C. Bommier, Z. Li, X. Ji. Hard Carbon Microspheres: Potassium-Ion Anode Versus Sodium-Ion Anode. Adv. Energy Mater., 2016, 6: 1501874.
[10] H. Kim, J. C. Kim, M. Bianchini, D. H. Seo, J. Rodriguez Garcia, G. Ceder. Recent Progress and Perspective in Electrode Materials for K-Ion Batteries. Adv. Energy Mater., 2018, 8: 1702384.
[11] I. Sultana, T. Ramireddy, M. M. Rahman, Y. Chen, A. M. Glushenkov. Tin-based composite anodes for potassium-ion batteries. Chem. Commun., 2016, 52: 9279.
[12] Q. Zhao, J. B. Wang, Y. Lu, Y. X. Li, G. X. Liang, J. Chen. Oxocarbon Salts for Fast Rechargeable Batteries. Angew. Chem. Int. Ed., 2016, 55: 12528.
[13] A. Eftekhari, Z. Jian, X. Ji. Potassium Secondary Batteries. ACS Appl. Mater. Interfaces, 2017, 9: 4404.
[14] L. Fan, Q. Liu, Z. Xu, B. Lu. An Organic Cathode for Potassium Dual-Ion Full Battery. ACS Energy Lett., 2017, 2: 1614.
[15] Y. Chen, W. Luo, M. Carter, L. Zhou, J. Dai, K. Fu, S. Lacey, T. Li, J. Wan, X. Han, Y. Bao, L. Hu. Organic electrode for non-aqueous potassium-ion batteries. Nano Energy, 2015, 18: 205.
[16] Z. Xing, Z. Jian, W. Luo, Y. Qi, C. Bommier, E. S. Chong, Z. Li, L. Hu, X. Ji. A perylene anhydride crystal as a reversible electrode for K-ion batteries. Energy Storage Mater., 2016, 2: 63.
[17] Q. J. Deng, J. F. Pei, C. Fan, J. Ma, B. Cao, C. Li, Y. D. Jin, L. P. Wang, J. Z. Li. Potassium salts of para-aromatic dicarboxylates as the highly efficient organic anodes for low-cost K-ion batteries. Nano Energy, 2017, 33: 350.
[18] C. Wang, W. Tang, Z. Yao, B. Cao, C. Fan. Potassium perylene-tetracarboxylate with two-electron redox behaviors as a highly stable organic anode for K-ion batteries. Chem. Commun., 2019, 55: 1801.
[19] C. Li, Q. J. Deng, H. C. Tan, C. Wane, C. Fan, J. F. Pei, B. Cao, Z. H. Wang, J. Z. Li. Para-Conjugated Dicarboxylates with Extended Aromatic Skeletons as the Highly Advanced Organic Anodes for K-Ion Battery. ACS Appl. Mater. Interfaces, 2017, 9: 27414.
[20] Y. Liang, C. Luo, F. Wang, S. Hou, S.-C. Liou, T. Qing, Q. Li, J. Zheng, C. Cui, C. Wang. An Organic Anode for High Temperature Potassium-Ion Batteries. Adv. Energy Mater., 2019, 9: 1802986.
[21] Q. Xue, D. Li, Y. Huang, X. Zhang, Y. Ye, E. Fan, L. Li, F. Wu, R. Chen. Vitamin K as a high-performance organic anode material for rechargeable potassium ion batteries. J. Mater. Chem. A, 2018, 6: 12559.
[22] Z. Jian, Y. Liang, I. A. Rodriguez-Perez, Y. Yao, X. Ji. Poly (anthraquinonyl sulfide) cathode for potassium-ion batteries. Electrochem. Commun., 2016, 71: 5.
[23] M. Tang, Y. Wu, Y. Chen, C. Jiang, S. Zhu, S. Zhuo, C. Wang. An organic cathode with high capacities for fast charge potassium-ion batteries. J. Mater. Chem. A, 2019, 7: 486.
[24] M. Xiong, W. Tang, B. Cao, C. Yang, C. Fan. A small-molecule organic cathode with fast charge-discharge capability for K-ion batteries. J. Mater. Chem. A, 2019, 7: 20127.
[25] Y. Hu, H. Ding, Y. Bai, Z. Liu, S. Chen, Y. Wu, X. Yu, L. Fan, B. Lu. Rational Design of a Polyimide Cathode for a Stable and High-Rate Potassium-Ion Battery. ACS Appl. Mater. Interfaces, 2019, 11: 42078.
[26] D. Li, W. Tang, C. Wang, C. Fan. A polyanionic organic cathode for highly efficient K-ion full batteries. Electrochem. Commun., 2019, 105: 106509.
[27] M. Chen, Q. Liu, Y. Zhang, G. Xing, S.-L. Chou, Y. Tang. Emerging polyanionic and organic compounds for high energy density, non-aqueous potassium-ion batteries. J. Mater. Chem. A, 2020, 8: 16061.
[28] J. D. Zhang, T. T. Liu, X. Cheng, M. T. Xia, R. T. Zheng, N. Peng, H. X. Yu, M. Shui, J. Shu. Development status and future prospect of non-aqueous potassium ion batteries for large scale energy storage. Nano Energy, 2019, 60: 340.
[29] C. Wang, W. Tang, S. Jia, Y. Yan, D. Li, Y. Hu, J. Gao, H. Wu, M. Wang, S. Liu, H. Lai, T. Zou, L. Xu, J. Xiong, C. Fan. Benzene-bridged anthraquinones as a high-rate and long-lifespan organic cathode for advanced Na-ion batteries Chem. Eng. J., 2021, 426: 131251.
[30] C. Zhang, Y. Xu, K. He, Y. Dong, H. Zhao, L. Medenbach, Y. Wu, A. Balducci, T. Hannappel, Y. Lei. Polyimide@Ketjenblack Composite: A Porous Organic Cathode for Fast Rechargeable Potassium-Ion Batteries. Small, 2020, 16: 2002953.
[31] M. Zhou, M. Liu, J. Wang, T. Gu, B. Huang, W. Wang, K. Wang, S. Cheng, K. Jiang. Polydiaminoanthraquinones with tunable redox properties as high performance organic cathodes for K-ion batteries. Chem. Commun., 2019, 55: 6054.
Cite This Article
  • APA Style

    Chuan Wang, Wu Tang, Cong Fan. (2021). Polyquinoneimides as Organic Cathodes for Advanced Potassium-Ion Batteries. International Journal of Energy and Power Engineering, 10(5), 79-86. https://doi.org/10.11648/j.ijepe.20211005.11

    Copy | Download

    ACS Style

    Chuan Wang; Wu Tang; Cong Fan. Polyquinoneimides as Organic Cathodes for Advanced Potassium-Ion Batteries. Int. J. Energy Power Eng. 2021, 10(5), 79-86. doi: 10.11648/j.ijepe.20211005.11

    Copy | Download

    AMA Style

    Chuan Wang, Wu Tang, Cong Fan. Polyquinoneimides as Organic Cathodes for Advanced Potassium-Ion Batteries. Int J Energy Power Eng. 2021;10(5):79-86. doi: 10.11648/j.ijepe.20211005.11

    Copy | Download

  • @article{10.11648/j.ijepe.20211005.11,
      author = {Chuan Wang and Wu Tang and Cong Fan},
      title = {Polyquinoneimides as Organic Cathodes for Advanced Potassium-Ion Batteries},
      journal = {International Journal of Energy and Power Engineering},
      volume = {10},
      number = {5},
      pages = {79-86},
      doi = {10.11648/j.ijepe.20211005.11},
      url = {https://doi.org/10.11648/j.ijepe.20211005.11},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ijepe.20211005.11},
      abstract = {Due to abundant raw materials, low cost and high theoretical energy density, organic potassium ion batteries (OPIBs) have attracted more and more attention from researchers as next promising battery system. However, some challenges still need to be solved. For example, most small-molecule organic electrode materials faced serious dissolution problem in liquid electrolytes, resulting in poor cycle stability. In particular, there are relatively few reports on the current cathodes with really excellent comprehensive performance (such as: high specific capacity, high working voltage, long life-span and excellent rate performance) for OPIBs. In this article, two polyanthraquinoneimide polymers were successfully synthesized and used as organic cathode materials for potassium ion batteries. Attributed to the large molecular structure of the polymer, PPAQ and PNAQ both were successful to be insoluble in the electrolyte (1 mol/L KPF6 in DME). After comparison, it was found that PNAQ exhibited better comprehensive electrochemical performance than PPAQ. At a current density of 100 mA/g, PNAQ achieved a stable discharge capacity of 138 mAh/g for 200 cycles and the retention rate was as high as 92%. At the same time, after 750 cycles at a high current density of 800 mA/g, the specific capacity of PNAQ still remained at 71 mAh/g with an average attenuation of only 0.03 mAh/g per cycle. Through an appropriate design process for the molecular structure, we proved that organic polymers could become excellent cathodes for potassium ion batteries.},
     year = {2021}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Polyquinoneimides as Organic Cathodes for Advanced Potassium-Ion Batteries
    AU  - Chuan Wang
    AU  - Wu Tang
    AU  - Cong Fan
    Y1  - 2021/10/16
    PY  - 2021
    N1  - https://doi.org/10.11648/j.ijepe.20211005.11
    DO  - 10.11648/j.ijepe.20211005.11
    T2  - International Journal of Energy and Power Engineering
    JF  - International Journal of Energy and Power Engineering
    JO  - International Journal of Energy and Power Engineering
    SP  - 79
    EP  - 86
    PB  - Science Publishing Group
    SN  - 2326-960X
    UR  - https://doi.org/10.11648/j.ijepe.20211005.11
    AB  - Due to abundant raw materials, low cost and high theoretical energy density, organic potassium ion batteries (OPIBs) have attracted more and more attention from researchers as next promising battery system. However, some challenges still need to be solved. For example, most small-molecule organic electrode materials faced serious dissolution problem in liquid electrolytes, resulting in poor cycle stability. In particular, there are relatively few reports on the current cathodes with really excellent comprehensive performance (such as: high specific capacity, high working voltage, long life-span and excellent rate performance) for OPIBs. In this article, two polyanthraquinoneimide polymers were successfully synthesized and used as organic cathode materials for potassium ion batteries. Attributed to the large molecular structure of the polymer, PPAQ and PNAQ both were successful to be insoluble in the electrolyte (1 mol/L KPF6 in DME). After comparison, it was found that PNAQ exhibited better comprehensive electrochemical performance than PPAQ. At a current density of 100 mA/g, PNAQ achieved a stable discharge capacity of 138 mAh/g for 200 cycles and the retention rate was as high as 92%. At the same time, after 750 cycles at a high current density of 800 mA/g, the specific capacity of PNAQ still remained at 71 mAh/g with an average attenuation of only 0.03 mAh/g per cycle. Through an appropriate design process for the molecular structure, we proved that organic polymers could become excellent cathodes for potassium ion batteries.
    VL  - 10
    IS  - 5
    ER  - 

    Copy | Download

Author Information
  • School of Materials and Energy, University of Electronic Science and Technology of China (UESTC), Chengdu, China

  • School of Materials and Energy, University of Electronic Science and Technology of China (UESTC), Chengdu, China

  • School of Materials and Energy, University of Electronic Science and Technology of China (UESTC), Chengdu, China

  • Sections